Recrystallized Silicon Carbide Sheet Sic Plate Kiln Furniture
Description
Basic Info
| Refractoriness (℃) | Refractoriness> 2000 |
| Feature | Long Time Materials, Instant Materials |
| Type | Refractory Material |
| Shape | Plate |
| Material | Sic |
| Sio2 Content | Above 85% |
| MGO Content | 0.2-1.3% |
| Application | Refractory Furnace Lining Insulation Materials |
| Density (Kg/M³ ) | 2.2-3.15g/cm3 |
| Feature 1 | Low Thermal Conductivity,Low Heat Storage |
| Feature 2 | Good Thermal Shock Resistance |
| Feature 3 | Reasonable Price |
| Transport Package | Standard One |
| Specification | Customized |
| Trademark | TK BRICKS |
| Origin | China |
| HS Code | 381600000 |
| Production Capacity | 3000000 PCS Per Month |
Product Description
Reaction bonded silicon carbide ceramic SIC wear liner plate for cyclone
Silicon Carbide kiln shelve is made of high quality synthetically made silicon carbide grains (SIC) Containing SiC72% to 99%.And selected bonding components, including oxidation bonded, Si3N4 bonded ,Sialon bonded , clay bonded etc.The product has a high temperature, high strength, volume stability and good thermal conductivity, acid,alkali and a variety of molten metal erosion ability and so on. widely used in colored aluminum tank, zinc vertical tank;metallurgical industry, blast furnace lining, ceramic kiln shelf panels,
Features:
1. High temperature resistant
2. Various sizes available
3. Competitive prices
4. Small tolorence: +-0.005mm
5. Good quality
6. Exact delivery time
| Item | RbSIC | SiSIC |
| Purity(%) | > 98 | >90 |
| Density(g/cm3 ) | 3.1-3.2 | >3.05 |
| Granularity(um) | 0.5-0.7 | 8--20 |
| Hardness(HRA) | ≥90 | ≥90 |
| Bending strength(MPa) | 400-580 | 350-450 |
| Compressive strength (MPa) | 3900 | >2500 |
| Fracture strength (MPa) | 3.05-4.6 | 4.3 |
| Modulus of elasticity(GPa) | 380-410 | 420 |
| Thermal comductivity | 102.6 | 35-110 |
| Coefficient of thermal expansion(1/ºC) | 4.02×10-6 | 4.3×10-6 |
| Poisson's ratio | 0.14 | 0.15 |
| Open porosity (%) | 7--8 | <0.1 |
| Temperature of application (ºC) | 1800 | 1410 |
| Item | SSIC |
| SIC Purity(%) | >98 |
| Bulk Density(g/cm3 ) | 3.06-3.15 |
| Max. Service Temp.(ºC) | 1800 |
| Compressive strength (Mpa) | ≥3900 |
| Bending strength(MPa) | 400-580 |
| Fracture strength(MPa) | 3.05-4.6 |
| Young's modulus(Gpa) | 380-410 |
| Thermal conductivity W/MK | 102.6 |
| Thermal expansion a(1/ºC) | 4.02x10 |
| Poisson's ratio | 0.14 |
| Apparent porosity % | 0 |
Product Photos: